News > Dynamic industry > Solving Residue Issues in Rubber Mold Release Agents: Silicone Oil Molecular Weight Is the Key Variable

Solving Residue Issues in Rubber Mold Release Agents: Silicone Oil Molecular Weight Is the Key Variable

In rubber manufacturing, surface tackiness, excessive coating thickness, or poor adhesion in subsequent painting or printing operations after applying mold release agents is often blamed on “improper spraying techniques.” However, recent application studies reveal that the root cause frequently lies in the inappropriate selection of silicone oil molecular weight in the release formulation. High-molecular-weight silicones form thick films and migrate slowly, leading to residue buildup; in contrast, low-molecular-weight silicones evaporate quickly and spread evenly—making them ideal for “trace-free demolding” applications.

“Many factories assume that the ‘thicker’ the silicone oil, the better the performance—but it’s actually the opposite,” notes an organosilicon application engineer. Experimental data show that when release agents are formulated with silicone oils having viscosities above 1000 cSt (high molecular weight), they form relatively thick films (>1.5 μm) on mold surfaces. Due to their long polymer chains and poor fluidity, these oils fail to spread uniformly and tend to accumulate in micrometer-scale patches. During vulcanization, portions migrate to the rubber surface, increasing the contact angle (>100°) and severely compromising downstream processes like painting, printing, or bonding.

Conversely, release agents based on low-molecular-weight silicones (50–300 cSt) form ultra-thin (<0.3 μm), dense, hydrophobic films on molds. These formulations level rapidly after spraying and partially volatilize, leaving minimal residue. Adhesion testing per ASTM D3359 demonstrates that rubber parts demolded with low-MW silicone agents achieve cross-hatch ratings of 4B–5B, whereas those treated with high-MW silicones typically score only 1B–2B.

“The goals of ‘long-lasting release’ and ‘zero residue’ are inherently contradictory,” experts caution. They recommend:

High-molecular-weight silicones (>1000 cSt) for large compression-molded parts and low-frequency demolding cycles where multiple releases without reapplication are desired.
Low-molecular-weight silicones (<300 cSt) for high-frequency, automated production lines—especially for components requiring secondary processing, such as seals and vibration dampers.

Several silicone suppliers now offer “demolding-specific” product lines with grades categorized by molecular weight and accompanied by post-spray surface energy test reports. One automotive rubber OEM reported a 70% reduction in paint rework rates after switching to a low-molecular-weight silicone-based release agent.

The industry is calling for a paradigm shift—from empirical, experience-driven release agent selection to a “molecular design–driven” approach—ensuring silicone oils truly operate “invisibly” within manufacturing workflows.