Lacquer general spraying construction. The color of colored aggregate particle size different, change order spraying construction can be made into various imitating natural stone decorative effect. If the decorative texture, the effect can be accompanied by the need to smear, rolling construction method.
(1) the closure of the grassroots
The purpose is to clean the grass-roots level, and penetrate into the grass-roots level, the capillary porosity of the grassroots, increase the strength and film bonding strength of the film. General use of roller coating construction, or spraying construction, finishing 2 times, can not have missed parts, uniform requirements.
(2) grassroots coloring process
The purpose of the increase of the coating's hiding ability, reduce the amount of paint, in order to achieve the decorative effect of natural stone. The main adhesion, durability, and water - resistant planar coatings (such as coatings for external use) are mainly used in the primary color treatment.. According to the determined color or model of natural stone color toning ingredient, grass-roots full roller coating or spraying 2 times primary colored paint, there must be no leak painting, through the imaginary parts. In order to achieve the decorative effect of the imitation stone block can be in the joint coating on the selected good grass-roots colored paint, in large area spraying truestonepaint bisection lattice joint parts should be completely occluded or scraping sewing processing.
(3) spraying
General 2 times spraying lacquer, coating uniformity, thickness below 3mm. The thickness of the coatings is more than 3mm, the texture is more abundant and the stone is stronger.. First of all, the paint consistency is appropriate, the first spray slightly dilute some of the paint, uniform, dry and then sprayed second times paint. When spraying, the paint is slightly thicker and thicker.. When after the spray bucket of material spraying with ejective gas will be sprayed finish blowing over the wavy pattern closer to to the effect of the natural stone, also can only by a thick coating will complete the decoration effect. If want to achieve the marble decorative effect, can be used double nozzle bucket construction, and spray two kinds of color, or with a single nozzle bucket respectively spray two kinds of color to color overlap, like hidden like this decorative effect. If it finds imitation stone decorative pattern smaller or bulges, before the available stainless steel trowel (or hard plastic trowel, hard plastics and) in the convex part of the rolling or pressure wiping, until it reaches the satisfactory results so far.
(4) cover handling
The paint spraying is completed, in order to protect the finishes, add gloss, improve pollution tolerance ability, prevent water to finish pore penetration and enhance the overall effectiveness of the decoration on the surface finishes can be transparent and coated with a silicone acrylic solvent based varnish treatment agent agent or silicone solvent type transparent varnish at treatment. After drying the water in its surface is bead like, hydrophobic sex is excellent, and will not become yellow in the course of use..
Reference dosage (kg/m2)
The basic 0.20.25 sealant
The basic 0.50.6 colorant
4 - 6 thin lacquer
Thick 6-8
Cover paint 0.6 - 0.4