  • IOTA 992 Silicone Structural Glazing Sealant

    IOTA 992 Silicone Structural Glazing Sealant

    1. Two components;  

    2. Structural sealing and glazing for curtain wall

    Features:

    1. Two parts , neutral cure to form an extremely tough elastomeric rubber ensuring a durable, flexible, and watertight bond 

    2. non-corrosive to metals, coated glass, low-E glass and many other substrates

    3. Excellent weatherability and high resistance to UV radiation ,heat and humidity, and ozone

    4. Excellent stability through wide temperature range from –50 ℃ to +150 ℃

    5. Excellent unprimed adhesion to wide range of substrates

    6. High level of mechanical properties

    7. Good compatibility with other neutral silicone sealants

     

    COLOURS

    Part A (base) of IOTA 992 is available in white, part B (curing agent) in black; Black color after mixing.

     

    PACKAGING

    IOTA 992 is available in kit: part A in 200L drums (net 190L), part B in 20L pails (net 18.5L). 

     

    SPECIFICATIONS

    IOTA 992 is designed to meet or even exceed the requirements of Chinese national specification GB16776-2005 Silicone Sealant for Structural Glazing Complies with ASTM C 1184

     

    Typical properties:

    These values are not intended for use in preparing specifications  

    Test Method

    Property

    Unit

    Standard

    Result  

    GB/T 13477 (ISO 7390)

    Slump

    mm

    ≤3

    0

    GB/T 13477 (ASTM D 2377)

    Tack free time

    h

    ≤3

    0.8

    GB/T 13477

    Working time (after 20 min.)

     

    ≤10

    2.2

    GB/T 531.1 (ISO 7619)

    53113477

    Hardness

    Shore A

    2060

    43

    GB 16776 (ASTM C 792)

    Heat Aging

     

     

     

    weight loss

    %

    ≤10

    3.5

    cracking

     

    Nil

    Nil

    chalking

     

    Nil

    Nil

    GB/T 13477 (ISO 8339)

    Tensile strength

    MPa

     

     

    23

     

    ≥0.60

    1.13

    90

     

    ≥0.45

    1.02

    -30

     

    ≥0.45

    1.62

    water immersion

     

    ≥0.45

    1.01

    water-UV exposure

     

    ≥0.45

    1.09

    adhesion failure

    %

    ≤5.00

    0

    extension rate at ultimate tensile strength at 23

    %

    ≥100

    140

    *GB: Chinese National Standard

    ASTM: American Society for Testing and Materials

    ISO: International Standardization Organization

    The “GB” testing method is equivalent or partly equivalent to that in the “()”

     

    STORAGE AND SHELF LIFE

    IOTA 992 should be stored at or below 27℃ in original unopened containers. It has a shelf life of 12 months from the date of manufacture.

     

    LIMITATIONS

    IOTA 992 should not be applied:

    To the materials that bleed oils, plasticizers or solvents, such as impregnated wood, oil-based caulks

    To frost laden or damp surfaces 

    For continuous water immersion

    When surface temperature below 4℃ or over 50℃  

     

    HOW TO USE

    Surface Preparation

    Clean all joints removing all foreign matter and contaminants such as oil, grease, dust, water, frost, old sealants, surface dirt, or glazing compounds and protective coatings.

     

    Mixing and Dispensing

    To obtain the optimal performance of IOTA 992, it is recommended that base and curing agent thoroughly mixed using an airless two-part silicone dispensing machine.

     

    IOTA 992 should be mixed at a ratio of 9:1~11:1 base to curing agent by volume; or 11:1~13:1 base to curing agent by weight.

     

    Lot matching of IOTA 992 base to curing agent is not required. Before use, it is recommended that curing agent be fully stirred to ensure the homogeneity of all components.

    992 part B curing agent will react with atmospheric moisture, therefore should not be exposed to air for prolonged periods of time.

     

    Priming

    Priming is not usually required when using IOTA 992. But it is essential that adhesion is tested prior to use to decide whether to use primer or not. 

     

    Masking and Tooling

    Areas adjacent to joint may be masked to ensure a neat sealant line. Do not allow mask tape to touch clean surfaces to which the silicone sealant is to adhere. Tooling should be completed in one continuous stroke after sealant application. Masking tape should be removed immediately after tooling.

     

    Equipment Cleaning

    When not being used, it is recommended that the dispensing equipment be purged either with the base component or flush with suitable solvent.



Feedback to "Iota Silicone Oil (Anhui) Co., Ltd."

  • *Name:
    *Contacts:
    *Content:
    *Code:    验证码

    Iota Silicone Oil welcome your message...

New Products

皖ICP备14007495号

Copyright © 2000-2024 Iota Silicone Oil (Anhui) Co., Ltd, All Rights Reserved